SAW
PF-H80AS/ US-80LT
SAW flux and wire combination
| Features: | - Suitable for welding of heavy duty structures
- Excellent impact value down to -80°C
|
|---|
| Classification: | AWS A5.23 F11A10-EG-G |
|---|
| Type of flux: | Bonded |
|---|
| Redrying of flux: | 250-350°Cx1h |
|---|
| Polarity: | DCEP |
|---|
Welding Positions:
Packaging data
| Flux | Mesh | Can | Wire | φ mm | Coil |
|---|
| PF-H80AS | 10x48 | 20kg | US-80LT | 3.2 | 25kg |
|---|
|
|
|
| 4.0 | 25kg |
|
|
|
| 4.8 | 25kg |
| Volume mm | 240W, 350H, 240L | Volume mm | 430W, 90H, 430L |
|---|
Composition (wire mass%)
| | Typical | Guarantya |
|---|
| C | 0.10 | 0.15 |
|---|
| Si | 0.11 | 0.25 |
|---|
| Mn | 2.03 | 1.75-2.25 |
|---|
| P | 0.007 | 0.015 |
|---|
| S | 0.004 | 0.015 |
|---|
| Ni | 2.59 | 2.40-2.90 |
|---|
| Mo | 0.74 | 0.60-0.90 |
|---|
| Cu | 0.12 | 0.40 |
|---|
| Note: aSingle values are maximium. |
Composition (weld metal mass %)
| | Typical | Guarantya |
|---|
| C | 0.06 | 0.12 |
|---|
| Si | 0.51 | 0.80 |
|---|
| Mn | 1.64 | 1.20-2.20 |
|---|
| P | 0.011 | 0.030 |
|---|
| S | 0.002 | 0.030 |
|---|
| Ni | 2.42 | 2.10-2.90 |
|---|
| Mo | 0.73 | 0.50-1.00 |
|---|
| Cu | 0.11 | 0.35 |
|---|
| Note: aSingle values are maximium. |
Weld mechanical properties
| | Typical | Guaranty |
|---|
| 0.2%YS (MPa) | 740 | 676min. |
|---|
| TS (MPa) | 860 | 759-896 |
|---|
| EI on 4d (%) | 23 | 15min. |
|---|
| IV -73°C (J) | 83 | 27min. |
|---|
| ABS | 4YQ690, MG |
|---|
| LR | 4Y69M(H5) |
|---|
| DNV | ⅣY69M (H5), MG |
|---|
| BV | 4Y69M H5, MG |
|---|
| CCS | 4Y69M H5, MG
|
|---|
| NK | KAW4Y69M,H5 |
|---|
| Note: Single electrode |