FCAW
MX-200H
Flux cored wire
| Features: | - Suitable for horizontal fillet welding by high speed tandem method (150cm/min)
- Excellent porosity resistibility to inorganic zinc primer
|
|---|
| Classification: | AWS A5.20 E70T-1C |
|---|
| Shielding gas: | CO2 |
|---|
| Polarity: | DCEP |
|---|
Welding Positions:
Packaging data
| φ mm | Drum |
|---|
| 1.4 | 200kg, 250kg |
| 1.6 | 200kg, 250kg |
| Volume mm | 530φ, 820H |
|---|
Composition (all-weld metal mass %)
| | Typical | Guarantya |
|---|
| C | 0.06 | 0.12 |
|---|
| Si | 0.55 | 0.90 |
|---|
| Mn | 1.55 | 1.75 |
|---|
| P | 0.01 | 0.03 |
|---|
| S | 0.01 | 0.03 |
|---|
| Ni | 0.01 | 0.50 |
|---|
| Cr | 0.02 | 0.20 |
|---|
| Mo | 0.01 | 0.30 |
|---|
| V | 0.01 | 0.08 |
|---|
| Cu | 0.02 | 0.35 |
|---|
| Note: aSingle values are maximium. |
Welding parameters (A)
| φ mm | 1F, 1G, 2F |
|---|
| 1.4 | 200-450 |
| 1.6 | 250-500 |
All-weld mechanical properties
| | Typical | Guaranty |
|---|
| 0.2%YS (MPa) | 500 | 400min. |
|---|
| TS (MPa) | 600 | 490-655 |
|---|
| EI on 4d (%) | 27 | 22min. |
|---|
| IV -18°C (J) | 90 | 27min. |
|---|
| Single | Tandem |
|---|
| ABS | 3Y400SA, H5 | 3Y400A, H5 |
|---|
| LR | 3YS, H5
| 3YM, H5 |
|---|
| DNV | ⅢYS | ⅢYM |
|---|
| BV | SA3Y40M, H5 | A3Y40M
|
|---|
| NK | KSW53Y40G (C) | KAW53Y40G (C) |
|---|
| CCS | - | 3YM
|
|---|