SAW
PF-H55AS/ US-36J
SAW flux and wire combination
| Features: | - Suitable for welding of structures for low temperature service
- Excellent impact value down to -60°C and CTOD at temperatures down to -20°C
|
|---|
| Classification: | AWS A5.17 F7A8-EH14, F7P8-EH14 |
|---|
| Type of flux: | Bonded |
|---|
| Redrying of flux: | 200-300°Cx1h
|
|---|
| Polarity: | DCEP |
|---|
Welding Positions:
Packaging data
| Flux | Mesh | Can | Wire | φ mm | Coil |
|---|
| PF-H55AS | 10x48 | 20kg | US-36J | 3.2 | 25kg | 76kg |
|---|
|
|
|
| 4.0 | 25kg
| 75kg
|
|
|
|
| 4.8 | 25kg
| 75kg
|
| Volume mm | 240W, 350H, 240L | Volume mm | 430W, 90H, 430L | 740W, 110H, 740L |
|---|
Composition (wire mass%)
| | Typical | Guarantya |
|---|
| C | 0.13 | 0.10-0.20 |
|---|
| Si | 0.01 | 0.10 |
|---|
| Mn | 2.00 | 1.70-2.20 |
|---|
| P | 0.007 | 0.030 |
|---|
| S | 0.008 | 0.030 |
|---|
| Cu | 0.10 | 0.35 |
|---|
| Note: aSingle values are maximium. |
Composition (weld metal mass %)
| | Typical |
|---|
| C | 0.07 |
|---|
| Si | 0.23 |
|---|
| Mn | 1.42 |
|---|
| P | 0.009 |
|---|
| S | 0.004 |
|---|
| Ti | 0.02 |
|---|
| B | 0.004 |
|---|
Weld mechanical properties
| | Typical | Guaranty |
|---|
| 0.2%YS (MPa) | 485 | 430 | 400min. |
|---|
| TS (MPa) | 555 | 530 | 483-655 |
|---|
| EI on 4d (%) | 33 | 31 | 22min. |
|---|
| IV -62°C (J) | 170 | 180 | 27min. |
|---|
| PWHT (°Cxh) | AW | 620x1 | AW & 620±15x1 |
|---|
| Single | Tandem |
|---|
| ABS | 5Y400 H5 | 5Y400 H5 |
|---|
| LR | 5Y40M, H5 | 5Y40M, H5 |
|---|
| DNV | ⅤY40M (H5),
VL2-4L, VL4-4L
| ⅤY40M (H5),
VL2-4L, VL4-4L
|
|---|
| BV | A5Y40M, H5 | A5Y40M, H5 |
|---|
| NK | KAWL3MH5 | KAWL3M H10 |
|---|